BSA-9005CJ is a high-density polyethylene-based black jacket compound with well-dispersed carbon black and stabilizers, designed for power and communication cable jacketing. It offers excellent melt strength, chemical resistance, ESCR, and superior performance across a wide temperature range.
ITEM CODE: BSA-9005CJ
Product: Black Jacket Compound
Carrier: High-Density Polyethylene
Active ingredient: Well dispersed Carbon Black+ Stabilizer
Application and Addition Rate: Jacketing of Power/Communication Cable: 100%
Advantages: This material offers good melt strength, superior mechanical properties across a wide temperature range, excellent processability, outstanding environmental stress crack resistance (ESCR), and strong chemical resistance.
Specifications: BSA-9005CJ meets the requirements of the following standards:
IEC 60502/ST7, IEC 60840/ST7, ASTM D-1248 type 3/Class C/Category 5/Grade J4/E8/E9
Physical-Mechanical Properties:
| Property | Unit | Value | Test Method |
|---|---|---|---|
| Density | gr/cm³ | 0.945± 0.03 | IEC 60811-606 or ISO 1183-1 |
| Melt Flow Rate (190°C/2.16 Kg) | g/10min | 0.3± 0.05 | IEC 60811-511 or ISO 1133-1 |
| Hardness, Shore D | - | Min. 58 | ISO 868 |
| Tensile Stress at Break | MPa | Min. 25 | IEC 60811-501 |
| Elongation at Break | % | Min. 600 | IEC 60811-501 |
| Carbon Black Content | % | 2.5±0.5 | IEC 60811-605 |
| Carbon Black Dispersion | - | Max. 2.5 | ISO 18553 |
| Oxidation Induction Time (200oC) | min | Min. 30 | ISO 11357-6 |
| Melting Temperature (DSC) | oC | Min. 127 | ISO 11357-3 |
| Resistance to Stress Cracking | hr | Min. 5000 | IEC 60811-406 |
| Water Absorption | % | Max. 0.01 | IEC 60811-402 |
| Brittleness Temperature | °C | Max. -75 | ISO 974 |
| UV Resistance Test | - | Pass | UL1581 |
| Vicat Softening Point | oC | Min. 120 | ISO 306 |
| Pressure Test at High Temperature | % | Max. 50 | IEC 60811-508 |
| Gray Scale after UV Resistance Test | - | 4-5 | ISO 105A02 |
| Thermal Aging in an air Oven @ 110°C (10 days) | MPa % |
Stress: Min. 21 Elongation: Min. 600 |
IEC 60811-401 |
| Dielectric Constant @ 1MHz | - | Max. 2.4 | IEC 60674-2 |
| Dissipation Factor @ 1MHz | - | Max. 0.005 | IEC 60674-2 |
| DC Volume Resistivity | Ohm-cm | Min. 1014 | IEC 60674-2 |
Processing Guideline: Our Best Temperature Profile is suggested Below:
| Drying Temp (Hopper) | 50°C-60°C |
| Zone 1 | 150°C-170°C |
| Zone 2 | 160°C-180°C |
| Zone 3 | 160°C-180°C |
| Zone 4 | 160°C-180°C |
| Head | 170°C-190°C |
| Die | 170°C-190°C |
Typical processing parameters are noted. Actual processing conditions depend on machine size, mold design, material residence time, etc.
Storage: Store in a dry place below 50 °C away from sun exposure, not to exceed more than 36 Months.
Packaging: Packed in 20 kg PP raffia bags on 1000 kg stretch-wrapped pallet.
Disclaimer: The information provided in this Technical Data Sheet is based on current knowledge and experience. The user is responsible for ensuring that the product suits their specific application. The manufacturer does not guarantee any particular properties or performance.